진동성형용 ρ-알루미나결합 알루미나 캐스터블 내화재료의 제조와 특성
천승호, 전병세
경남대학교 신소재공학부
Preparation and Properties of ρ-alumina Bonded Alumina Vibrated Castable Refractory
The special binding mechanism developed provides higher density, lower porosity and higher strengths compared with conventional castables. $rho$-alumina was employed as a binder materials and nano-sized clay colloidal was added to enhance the drying strength preparing for the alumina vibrated castable. Lower water requirement for casting results in a denser product. The mechanical properties with dimensional stability and corrosion resistance behaviors have been improved by controlling the matrix compositions of the castable. The modulus of rupture and compressive strength after heat treatment at 150$0^{circ}C$ are 92.34 kgf/$textrm{cm}^2$ and 370 kgf/$textrm{cm}^2$ respectively. The activation energy of mullite formation is 11.47 kcal/mol.섂돀胊ﺖ⨀塨
Key words: $\rho$-alumina, Nano-sized clay, Alumina vibrated castable
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI