SiC가 코팅된 그라파이트 Foam의 제조 및 특성 분석
경재진, 김정주, 김수룡, 권우택, 조광연, 김영희
요업기술원 환경재료팀
Preparation and Characterization of SiC Coated Graphite Foam
Jae-Jin Kyung, Jung-Ju Kim, Soo-Ryong Kim, Woo-Teck Kwon, Kwang-Youn Cho, Young-Hee Kim
Eco-Materials Team, Korea Institute of Ceramic Engineering and Technology
Graphite is widely used in electronic industry due to its excellent electrical and thermal properties. However, graphite starts to oxidize around $400^{circ}C$ that seriously degrades its properties. SiC coating can be applied to graphite foam to improve its high temperature oxidation resistance. In this research, SiC coating on graphite foam was made via preceramic polymer using a polyphenylcarbosilane. 20% of polyphenylcarbosilane in hexane solution was coated onto graphite by dip coating method. Thermal oxidation was carried out at $200^{circ}C$ for crosslink of the preceramic polymer and the sample were pyrolysized at $800^{circ}C{sim}1200^{circ}C$ under nitrogen to convert the preceramic polymer to SiC film. The microstructure of the SiC coating after pyrolysis was investigated using FESEM and oxidation resistance up to $800^{circ}C$ was evaluated.
Key words: Graphite foam, SiC coating, Heat sink, High Temperature
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI