La0.8Ca0.2Cr0.98O3 powder was prepared using the modified Pechini process. Various crystalline phases formed during thermal decomposition were investigated. (La,Ca)CrO4 phase, first formed from the precursor, was transformed to (La,Ca)CrO3 and CaCrO4 above 80$0^{circ}C$, which remained up to 110$0^{circ}C$. However, only (La,Ca)CrO3 phase consisting of orthorhombic and intermediate rhombohedral polymorphs was observed after sintering at 125$0^{circ}C$. The specimens sintered at 140$0^{circ}C$ exhibited 98% of relative density and rather wide grain size distribution with average grain size of 3-4 ${mu}{textrm}{m}$. Densification and grain growth of the specimens observed above 125$0^{circ}C$ were presumably attributed to liquid phase sintering resulted from melting of Ca3(CrO4)2 phase.
Key words: SOFC, Lanthanum calcium chromite, Crystalline phase, Thermal decomposition
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI