산화 주석 후막에 대하여
서울대학교 요업공학과
On the Stannic Oxide Thick Film
Thick film resistor paste was made utilizing oxide materials such as SnO, SnO+Sb2O3, and SnO+Zn. The oxide materials were mixed respectively with Q-12 glass powder and finally suspended in ethyl cellulose dissolved in ethyl cellosolve. Thick film resistor was made by screen printing the paste on the alumina substrate and firing it at a suitable temperature. Among thick films made from the resistor paste, the thick film containing 85% SnO and fired at $600^{circ}C$ demonstrated the finest electrical properties showing 10 K ohm in sheet resistance, 110 ppm/$^{circ}C$ in TCR. In general, TCR of the thick films made from the oxide-mixture paste is good in linearity, therefore it is suggested the oxide-mixture paste is utilized as the negative thermistor.
PDF Links  PDF Links
Full text via DOI  Full text via DOI
Download Citation  Download Citation
CrossRef TDM  CrossRef TDM
Related article
On the Stannic Oxide Thin Film  1976 ;13(2)
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI