| Properties of Dye Sensitized Solar Cells with Adding Nano Carbon Black into Blocking Layer |
| Kwangbae Kim, Yunyoung Noh, Ohsung Song |
| Department of Materials Science and Engineering, University of Seoul |
|
|
|
|
|
| ABSTRACT |
|
Blocking layers with nano carbon blacks (NCBs) were prepared by adding 0.0 ~ 0.5 wt% NCBs to the $TiO_2$ blocking layer. Then, dye sensitized solar cells (DSSCs) were fabricated with a $0.45cm^2$ active area. TEM and micro-Raman spectroscopy were used to characterize the microstructure and phases of the NCBs, respectively. Optical microscopy and AFM were used to analyze the microstructure of the $TiO_2$ blocking layer with NCBs. UV-VIS-NIS spectroscopy was used to determine the band gap of the $TiO_2$ blocking layer with NCBs. A solar simulator and potentiostat were used to determine the photovoltaic properties and impedance of DSSCs with NCBs. The energy conversion efficiency (ECE) increased from 3.53 to 6.20 % when the NCB content increased from 0.0 to 0.3 wt%. This indicates that the effective surface area and electron mobility increased in the $TiO_2$ blocking layer with NCBs. However, the ECE decreased when the NCB content was increased to over 0.4 wt%. This change occurred because the effective electron transport area decreased with the addition of excessive NCBs to the $TiO_2$ blocking layer. The results of this study suggest that the ECE of DSSCs can be enhanced by adding the appropriate amount of NCBs to the $TiO_2$ blocking layer. |
| Key words:
Nano carbon black, Blocking layer, Energy conversion efficiency, Dye sensitized solar cell |
|
|
|
PDF Links
Full text via DOI
Download Citation 