하소이트리아 소결체의 특성과 플라즈마저항성 평가
최진삼, Tadachika Nakayama1, 배원태
경상대학교 세라믹공학전공
1나가오카과학기술대학 극한에너지 밀도공학연구센타
Plasma Resistance Evaluation and Characteristics of Yttria Ceramics Sintered by Using Calcination Yttria
Jinsam Choi, Tadachika Nakayama1, Won Tae Bae
Department of Ceramic Engineering, Gyeongsang National University
1Department of Electrical Engineering/Electronic Devices and Optical Electronics group, Nagaoka University of Technology
ABSTRACT
The evaluation of plasma resistance and the characteristics of yttria ceramics fabricated by calcination yttria as a starting material without dopants under an oxidation atmosphere was investigated. Regardless of the starting materials, as-received, and calcined yttria powder, XRD patterns showed that all samples have $Y_2O_3$ phase. The three cycling process inhibited a large grain, which occurs frequently during the yttria sintering, and a high density ceramic with a homogeneous grain size was obtained. The grain size of the sintered ceramic was affected by the starting powders. The smaller the grain size, the larger were the Young's modulus and KIC. Compared to $Al_2O_3$ and $ZrO_2$ ceramics, yttria ceramics showed a 3 times larger plasma resistance and a 1.4~2.2 times lower weight loss during the plasma etching test, respectively.
Key words: As-received Yttria, Calcined Yttria, Homogeneous Grain, Plasma Resistance
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI