Journal of the Korean Ceramic Society 2009;46(1): 24.
doi: https://doi.org/10.4191/kcers.2009.46.1.024
BLU 및 형광체 코딩용 알루미나 분산액의 제조 및 평가
유정환, 정승화1, 홍경표1, 문종수, 강종봉
경남대학교 대학원 재료공학과
1(주) 쎄노텍 부설 부품소재개발 연구소
Fabrication of Alumina Suspension for Coating of BLU(Back Light Units) and Fluorescent Substances
Jeong-Hwan Yu, Seung-Hwa Jung1, Gyung-Pyo Hong1, Jong-Soo Mun, Jong-Bong Kang
Department of Materials Science and Engineering of Kyungnam University
1Component Materials Research Institute, Cenotec Co. Ltd.
The suspension of $Al_2O_3$ which has long-term stability was made by mechanical milling. Thin films were evaluated and made to use as coating materials. A particle size of the suspension manufactured was 98 nm when 2 mt% nitric acid was added. It indicated that viscosity of the suspension is 12 cps and that it had the long-term stability. Thickness which was from 200 nm to 600 nm of the thin films was able to be made by adjusting draw rate and organic additive. Cracks of thin films at room temperature were prevented by adding Ethyl cellulose from 0.5 wt% to 2 wt%. The thin film heated at $500^{circ}C$ indicated a hydrophilic property against water and an excellent permeability against a visible ray.
Key words: $Al_2O_3$, Alumina thin films, Ceramic coating
PDF Links  PDF Links
Full text via DOI  Full text via DOI
Download Citation  Download Citation
CrossRef TDM  CrossRef TDM
Related article
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI