Zn-Pr-Co-Cr-La 산화물계 비선형 저항체의 전기적, 유전적 성질에 소결온도가 미치는 영향
남춘우
동의대학교 전기공학과
Influence of Sintering Temperature on Electrical and Dielectric Characteristics of Zn-Pr-Co-Cr-La Oxide-Based Nonlinear Resistors
Choon-Woo Nahm
Department of Electrical Engineering, Dongeui University
ABSTRACT
The electrical and dielectric properties of $ZnO-Pr_6O_{11}CoO-Cr_2O_3La_2O_3-based$ nonlinear resistors were investigated at different sintering temperatures in the range of $1230{sim}1300^{|circ}C$. As the sintering temperature increased, the breakdown voltage decreased from 777.9 to 108.0V/mm, the nonlinear coefficient greatly decreased from 77.0 to 7.1, and the leakage current increased from $0.4{mu}A;to;50.6{mu}A$. On the other hand, the donor density from $0.90{times}10^{18};to;2.59{times}10^{18}/cm^3$ and the barrier height decreased from 1.89 to 0.69 eV with increasing temperature. The dielectric dissipation factor increased from 0.0879 to 0.2839 for the increase of sintering temperature.
Key words: Sintering temperature, Electrical properties, Nonlinear resistors
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI