Microstructure and Mechanical Properties of Alumina/Zirconia Layered Composites
Seung-Woo Lyu, Young-Min Park, Tae-Young Yang, Su-Chak Ryu1, Young-Woo Kim2, Seog-Young Yoon, Hong-Chae Park
School of Materials Science and Engineering, Pusan National University
1Department of Nano Information Materials Science and Engineering, Pusan National University
2Functional Materials Research Team, Research Institute of Industrial Science and Technology
Symmetric three-layer $Al_2O_3/ZrO_2$ composite has been prepared by freeze casting and pressureless sintering at $1400-1600^{circ}C$ in air. The layered material sintered at $1600^{circ}C$ showed the maximum fracture strength (410 MPa), measured by a four-point bending test. Contact damage strength was superior in three-layer composite compared with corresponding mono-layered material, possibly due to the development of relatively large compressive stress. The grain growth of $ZrO_2$ particles was mainly governed by coalescence mechanism.
Key words: Symmetric three-layer $Al_2O_3/ZrO_2$ composite, Freeze casting
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI