산 에칭에 의한 BaO-B2O3-ZnO계 유리조성물의 용출 현상 |
김재명, 홍경준1, 김남석, 김형순 |
인하대학교 신소재공학부 1(주)휘닉스 PDE 기술연구소 |
Dissolution Phenomenon in BaO-B2O3-ZnO Glass System by Acid Etching |
Jae-Myung Kim, Kyung-Jun Hong1, Nam-Suk Kim, Hyung-Sun Kim |
School of Materials Engineering, Inha University 1R&D Center, Phoenix PDE |
|
|
|
ABSTRACT |
For producing the fine ribs structure of plasma display panel, the metal ions of barrier materials during the etching process should be understood on the etching mechanism with etching conditions. Etching was done on bulk glasses of the $BaO_B_2O_3-ZnO$ system with $HNO_3$ solution at $40^{circ}C$. The surface structure of glasses and ion dissolution were analyzed by ICP (Inductive Coupled Plasma measurement). The structure and surface of the etched bulk glass were investigated by using scanning electron microscopy and nanoindenter. As a result, Ba (3-35 ppm/min) and Zn (2-27 ppm/min) ions as major components were leached in the solution and the leached layers were found to be phosphor-rich surface layers. A decrease of the bridge oxygen and relative increase of non bridge oxygen in the etched glass were found by X-ray photoelectron spectroscopy. |
Key words:
Etching glass, Dissolution, Glass, Metal ion, Leaching |
|
|
|