전이금속염 첨가에 의한 판상 α-Al2O3 결정체 제조
송효경, 박병기, 이정민
한국화학연구원 화학공정 연구센터
Preparation of Flaky α-Al2O3 Crystals by Transition Metal Salts Addition
Hyo-Kyung Song, Byung-Ki Park, Jung-Min Lee
Center of Chemical Engineering, Korea Research Institute of Chemical Technology
[ ${alpha}-Al_2O_3$ ] precursor was synthesised by sol-gel method using aluminum sulfate, sodium sulfate and sodium carbonate as law materials. The flaky ${alpha}-Al_2O_3$ crystals were prepared by heating using precursor about $1,050^{circ}C$. In this study, the effect of some transition-metal sulfate ($FeSO_4,;SnSO_4,;ZnSO_4$) addition have been investigated. When iron sulfate was added, it could see that act on impurities in crystal growth process. In case of tin sulfate, distribution of Platelets was very broad. When flaky ${alpha}-Al_2O_3$ crystals were prepared zinc sulfate addition, thickness, size, and distribution of platelets was suited to industrial application. The average diameter of flaky ${alpha}-Al_2O_3$ crystals was about 20 $mu$m, and its thickness was about 0.3 $mu$m. Increasing addition of zinc sulfate, thickness of ${alpha}-Al_2O_3$ platelet was decreased.
Key words: Flaky, Pseudo-boehmite, Alumina, Pearlescent substrate, Filler
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI