질화규소의 미세조직과 기계적 성질에 미치는 h-BN 첨가의 영향
김승현, 이영환, 조원승, 김준규1, 조명우2, 이은상2, 이재형3
인하대학교 재료공학부
1인하대학교 소재연구소
2인하대학교 기계공학부
3영남대학교 재료금속공학부
Effect of h-BN Content on Microstructure and Mechanical Properties of Si3N4
$Si_{3}N_{4}$-BN based machinable ceramics were fabricated by hot-pressing at $1800^{circ}C$ for 2 h under a pressure of 25 MPa. The microstructure, mechanical properties, and machinability were investigated. With increasing h-BN content from 5 vol% to 30 vol%, three point flexural strength decreased from 1000 MPa of monolithic S $i_3$ $N_4$ to 720~400 MPa. The fracture toughness, $K_{IC}$ , was decreased from 7.6 MPaㆍ$m^{1/2}$ of monolithic S $i_3$ $N_4$ to 6.5~4.1 MPaㆍ$m^{1/2}$. The grain size and aspect ratio of $beta$-S $i_3$ $N_4$ slightly decreased with increasing h-BN content. S $i_3$ $N_4$ monolith could not be machined due to brittle fracture, but S $i_3$ $N_4$-BN based machinable ceramics could be machined without fracture, showing excellent machinability. With increasing h-BN content, the thurst force during cutting and micro-drilling process was decreased.
Key words: Machinable ceramics, $Si_3$$N_4$, h-BN, Mechanical property, Machinability
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI