BaZrO3계 수소이온 전도체의 제조 및 첨가물에 따른 전기적 특성
권정범, 유광수
서울시립대학교 신소재공학과
The Fabrication of BaZrO3-based Proton Conductors and their Electrical Properties by Dopants
BaZr $O_3$-based proton conductors in which B-site cations are partially substituted by Ce and Yb were fabricated by a solid state reaction method. The electrical properties of the specimens were measured by using impedance analyzer in dry air and wet air atmospheres. The electrical conductivity showed higher value in wet air than in dry air at below $600^{circ}C$. As the Ce content increased, the electrical conductivity increased. Among four compositions, BaZ $r_{0.8}$C $e_{0.15}$Y $b_{0.05}$ $O_3$$_{-{delta}}$ specimen showed the highest electrical conductivity,1.72$times$10$^{-3}$ S$cm^{-1}$ /, at 80$0^{circ}C$. In the low temperature region, the electrical conductivity was higher in wet air than in dry air. However, as the temperature increased, the proton conductivity reduced and thus the electrical conductivity showed similar value at approximately $700^{circ}C$.>.>.>.
Key words: $BaZrO_3$, Proton conductor, Electrical conductivity, Impedance analysis
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI