고온 반응에 의한 Ti3AlC2합성 |
황성식, 박상환1, 한재호1, 한경섭1, 김태우2 |
국민대학교 자동차공학과 1한국과학기술연구원 복합기능세라믹스연구센터 2국민대학교 기계설계학과 |
Reaction Synthesis of Ti3AlC2 at High Temperature |
|
|
|
|
|
ABSTRACT |
$Ti_3AlC_2$was synthesized from TiCx and Al powder as a starting materials at the temperature range between$800^{circ}C;and;1500^{circ}C$. The vacuum sintering and hot pressing methods were imployed to synthesize$Ti_3AlC_2$. The high purity$Ti_3AlC_2$was synthesized using TiCx and Al powder as starting materials without formation of Ti-Al intermetallic compound and Al-C compound.$Ti_2$AlC and$Ti_3AlC_2$were preferentially synthesized at$800^{circ}C$and above$1200^{circ}C$, respectively.$Ti_2$AlC formed at low temperature was transformed to$Ti_3AlC_2$by further reaction with TiC. In this study, the synthesis mechanism for$Ti_3AlC_2$was proposed. The synthesized$Ti_3AlC_2$showed the nano laminating structure consisting of$Ti_3AlC_2$crystal with the thickness of 45~120 nm. ᨑⴀ 㘱㜮㔸㔰㔹㬅K䍄乍툗ਆ |
Key words:
${Ti_3}{AlC_2}$, TiCx, Nano laminating structure |
|
|
|