Glass첨가에 의한 BaO-Nd2O3-TiO2계 세라믹스의 저온소결과 마이크로파 유전특성
신동순, 최영진, 박재환1, 남산, 박재관1
고려대학교 재료공학과
1한국과학기술연구원 복합기능세라믹스연구센터
The Effect of Glass Addition on the Sintering and Dielectric Properties of BaO-Nd2O3-TiO2 Microwave Ceramics
The effect of glass addition on the low-temperature sintering and microwave dielectric properties in $BaO-Nd_2O_3-TiO_2$ dielectric ceramics were studied. When 10~30 wt% of alkali lithium borosilicate glass was added, the sintering temperature decreases from $1300^{circ}C$;to;1000^{circ}C$ and the relative density more than 95% was obtained. When the added amount of glass increased above 10 wt%, the density as well as dielectric properties changed, which was attributed to the second phase formation. When the sample was sintered at 100$0^{circ}C$ with l0wt% of glass, the dielectric properties of $Qxf_o{ge}2800,;{varepsilon}_r{ge}65;and;{ au_f=+55 ppm/^{circ}C$ were obtained.저ꢕ잖⨀ꂕ잖⨀梓
Key words: $BaO-{Nd_2}{O_3}-{TiO_2}$, Low temperature sintering, Borosilicate glass, LTCC, Second phase
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI