Silicon carbide candle filters for the pressurized fluidized bed combustion system were fabricated by extrusion process. Carbon black was added to control the porosity. Inorganic additives such as clay and calcium carbonate were added to exhibit appropriate strength. Silicon carbide layer with a finer pore size (mean pore diameter ~$10{mu}m$) was coated on the silicon carbide support layer (mean pore diameter ~$47{mu}m$, porosity ∼40%). After that, the filter was sintered at 1400${circ}C$ in air. We evaluated the filtration performances of the filter at 500${circ}C$ and $5kgf/cm^2$ of pressure. As a result, high separation efficiency, >99.999% was measured. It is expected that silicon carbide candle filter can be successfully used for the pressurized fluidized bed combustion system. |
Key words:
Pressurized fluidized bed combustion, Silicon carbide, Hot gas filter, Candle typed filter, Extrusion, Separation efficiency |
|