Journal of the Korean Ceramic Society 2002;39(9): 851.
doi: https://doi.org/10.4191/kcers.2002.39.9.851
MoO3가 첨가된 Cr2O3 플라즈마 용사코팅의 고온 마찰 마멸 특성
여인웅, 안효석, 임대순1
한국과학기술연구원 트라이볼로지연구센터
1고려대학교 재료공학과
Friction and Wear Properties of Plasma-sprayed Cr2O3-MoO3 Composite Coatings at High Temperature
In-Woong Lyo, Hyo-Sok Ahn, Dae-Soon Lim1
Tribology Research Center, Korea Institute of Science and Technology
1Department of Material Science and Engineering, Korea University
ABSTRACT
Tribological behavior of plasma-sprayed $Cr_2O_3$-based coatings containing $MoO_3$ at 450$^{circ}C$ was investigated to understand the influence of $MoO_3$. A reciprocal disc-on-plate type tribo-tester was employed to examine fricition and wear behavior of the specimens. The microstructure and phase composition of the coating was characterized with Transmission Electron Microscopy(TEM). The TEM analysis indicated that $MoO_3$ was dispersed into the grain boundary, resulting in the increase of the hardness and density of the coating. Worn surfaces were investigated by scanning electron microscopy and chemistry of the worn surfaces was analyzed using a X-ray Photoelectron Spectrometer(XPS). The results showed that the friction coefficient of the $MoO_3$-added coatings was lower than that without $MoO_3$ addition. The larger protecting layers were observed at the worn surface of plasma spray coated specimens with $MoO_3$ composition in the protecting layer appears to be more favorable in reducing the friction.
Key words: Plasma-sprayed coatings, $Cr_2O_3$, $MoO_3$, Friction, Wear
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI