Synthesis of $TiO_2$Anchored on a Porous Clay Ceramic Support Using Dropping Precipitant Method
TiO$_2$anchored on a porous clay ceramic support (PCS) for use in lightweight photocatalyst were synthesized by the dropping precipitant method. A PCS of macro and micro pore size of around several mm~${mu}{textrm}{m}$ in diameter were prepared by the rapid heat treatment at, 1,15$0^{circ}C$ for 10 min from low grade of clay. The change in pH of reaction solution due to the different addition rate of NH$_4$HCO$_3$as a precipitant, the reaction temperature and the concentration of TiCl$_4$had a pronounced effect on the nature of precipitated TiO$_2$particles on the surface of a PCS and the crystal structure of precipitated TiO$_2$particles. At an addition rate of 0.8 ml/min of NH$_4$HCO$_3$and pH=6 of reaction solution, homogeneous precipitation of TiO$_2$particles on a PCS was achieved. TiO$_2$particles with anatase phase was precipitated on the surface of a PCS at the low concentration of TiCl$_4$, the high addition rate of NH$_4$HCO$_3$and the high reaction temperature.
Key words: Photocatalyst, Anatase phase, Porous clay ceramic support(PCS), Dropping precipitant method
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI