Mn-Co-Ni 산화물계 NTC 서미스터의 조성에 따른 전기적 특성과 경시변화
권정범, 정용근1, 엄우식1, 송준광2, 유광수
서울시립대학교 재료공학과
2산업기술시험원 재료평가팀
The Electrical Properties and Aging Effects on the Composition of Mn-Co-Ni NTC Thermistors
Mn-Co-Ni oxide system has been used as the NTC thermistors for normal temperature applications. Mn-Co-Ni oxide-based thermistors with various compositions were sintered at 1250$^{circ}C$ for 3 hours and then maintained at 1000$^{circ}C$ for 3 hours. The electrical properties of the thermistors fabricated were measured. In particular the MCN622 composition (Mn$_3$O$_4$60 wt%, Co$_3$O$_4$20 wt%, NiO 20wt%) exhibited the lowest resistivity and relatively high B constant. The MCN721 composition (Mn$_3$O$_4$70wt%, Co$_3$O$_4$20wt%, NiO 10 wt%) showed the higher resistivity than any other compositions. The aging properties of each composition showed comparatively stable characteristics within ${pm}$2%.
Key words: NTC thermistor, Mn-Co-Ni oxide, Aging properties
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI