J. Korean Ceram. Soc. > Volume 37(2); 2000 > Article
Journal of the Korean Ceramic Society 2000;37(2): 174.
침투된 지르코니아-뮬라이트 복합체의 미세구조 및 기계적 성질
손영권, 이윤복1, 김영우2, 오기동1, 박홍채1
1부산대학교 재료공학부
Microstructure and Mechanical Properties of Infiltrated Zirconia-Mullite Composite
Y-TZP/mullite composites were prepared by the infiltration of Y-TZP precursor into partially reaction-sintered mullite. The addition of Y-TZP(~7.2 wt%) increased the bend strength(207 MPa), fracture toughness(4.6MPa.m1/2) and Vickers microhardness(853kg/$textrm{mm}^2$) of the uninfiltrated mullite sintered at 162$0^{circ}C$ for 10h by more than 75, 70 and 105%, respectively. Residual alumina-rich glass was observed at a mullite/mullite junction, due to the mullitization reaction of silica melt with crystalline $alpha$-Al2O3 during a final sintering. Although ZrO2 inclusions improved the final sintered density of mullite they did not effectively prevent its grain growth.
Key words: Y-TZP/mullite composites, Infiltration, Y-TZP precursor, Partially reaction-sintered mullite
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI