Journal of the Korean Ceramic Society 1999;36(7): 679.
SrZr$_{0.95}$M$_{0.05}$O$_3$-$delta$ 및 BaZr$_{0.95}$O$_3$-$delta$(M=Ga, Y) 의 제조와 전기적 특성
편영미, 유광수
서울시립대학교 재료공학과
Fabrication and Electrical Characteristics of SrZr$_{0.95}$M$_{0.05}$O$_3$-$delta$ and BaZr$_{0.95}$O$_3$-$delta$(M=Ga, Y)
Specimens of SrZr0.95Ga0.05O3-$delta$, SrZr0.95Y0.05O3-$delta$, BaZr0.95Ga0.05O3-$delta$ and BaZr0.95Y0.05O3-$delta$ were fabricated by a solid-state reaction method and subsequent sintering at 150$0^{circ}C$ to 1$600^{circ}C$ The microstructures and electrical characteristics of the specimens were studied. Only BaZr0.95Ga0.05O3-$delta$ showed dense microstructure and had typical impedance spectra at various temperature. Its electrical conductivity by impedance analysis was 2.7$times$10-3$Omega$-1.cm-1 at 90$0^{circ}C$ in air. The BaZr0.95Ga0.05O3-$delta$ exhibited lower grain rsistance in wet atmosphere than in dry atmosphere and the reduction of resistance is due to the proton conduction.
Key words: Proton conductor, Impedance Spectroscopy, Electrical conductivity
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI