알콕사이드 가수분해법에 의핸 제조된 TiO$_2$ 분말을 이용한 Micad의 표면 개질
한상필, 윤영훈, 이상훈1, 최성철
한양대학교 무기재료공학과
1대한광업진흥공사 기술연구소
Surface Modification of Mica Using TiO$_2$ prepared by Alkoxide Hydrolysis Method
TiO2 powder was adsorbed on the surface of mica using the heterocoagulation method in water TiO2 powder was prepared from hydrolysis of titanium-iso propoxide in a mixed solvent of anhydrous ethanol and water. When the molar ratio of water to titanium iso-propoxide was 0.25 monodispersed spherical TiO2 particles were obtained. The prepared TiO2 powder showed anatase phase after heat treatment at 50$0^{circ}C$ for 2 h and then transformed to rutile phase after heat treatment at 100$0^{circ}C$ for 2h. The iso-electric points of TiO2 and Mica were pH 3.9 and pH 3.25 respectively which were measured by the Z-potential analysis in water base. The maximum Z-potential difference between two powders was observed in the range of pH 3.6~3.7 TiO2 powder was adsorbed on the surface of mica by heterocoagulation method in pH 3.6~3,7 The properties of prepared TiO2 powder was haracterized by TG-DTA, XRD and SEM The morphology and thermal properties of TiO2-adsorbed mica were examined.
Key words: Alkoxide, Heterocoagulation, Hydrolysis, Zeta-potential
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI