Journal of the Korean Ceramic Society 1999;36(5): 531.
핏치계 탄소-탄소 복합체의 제조 미세구조 및 마찰-마모 특성
이진용, 서동수, 임연수1, 조동환2
충남대학교 재료공학과
1명지대학교 세라믹·화학공학부
2금공공과대학교 고분자공학과
Fabrication Microstructure and Friction-Wear Properties of Pitch-Based C-C composites
This study presents microstructure and friction-wear properties of pitch-based C-C composites prepared by a vacuum impregnation-atmospheric carbonization (VICA) and a hot isostatic pressure impregnation-carbonization (HIPIC) process. For the VIAC process the density was 1.79g/cm3 after 5 times of densification cycle. On the other hand 1.83g/m3 only after 3 times of densification cycle by the HIPIC. The VIAC C-C composites. showed high friction coefficient and wear rate due to a low hardness as a result high crystallinity of the composites. In the VIAC C-C composites the friction coefficient and the rate decreased with increasing sliding velocity and normal load for all friction condictions except the condition of 123.3N-5.86 msec-1 where the wear rate increased rapidly by an oxdation wear that was resulted from a high friction temperature at this condition
Key words: Coal-tar pitch, VIAC, HIPIC, C-C composites, Friction coefficient, Wear rate
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI