J. Korean Ceram. Soc. > Volume 36(2); 1999 > Article
Journal of the Korean Ceramic Society 1999;36(2): 130.
고로 슬래그 시멘트의 저온 조기 강도 증진
장복기, 임용무1, 김윤주2
전남대학교 세라믹공학과
1전남대학교 세라믹학과
2동신대학교 세라믹공학과
Improvement of Early Strength of Blast-Furnace Slag Blended Cement at Low Temperature
ABSTRACT
The enhanced slag fineness and the batch water of low water-to-cement ratio(W/C) were employed in order to improve the early strength of blast-furnace slag blended cement at low temperature. A grinding aid was used to grind the blast-furnace slag into the fineness of 6,280$textrm{cm}^2$/g (Blaine), and this fine slag was then homogeneously mixed with the ordinary Portland cement to produce the blast-furnace slag blended cement containing 40% slag by weight composition. On the other hand, the batch water could be reduced from W/C=0.50 (KS L 5105) to W/C=0.33 through a commercial, naphthalene type superplasticizer. Through the method mentioned above, the early strength of the blast-furnace slag blended cement at low temperature could be enhanced even somewhat higher than the Portland cement strength. And the microsturcture of the cement was studied by both the pore structure analysis and the A.C. impedance measurement.
Key words: Blast furnace slag cement, Low curing temperature, Early-high strength, Pore structure analysis, A.C. impedance spectroscopy
TOOLS
PDF Links  PDF Links
Full text via DOI  Full text via DOI
Download Citation  Download Citation
CrossRef TDM  CrossRef TDM
  E-Mail
Share:      
METRICS
618
View
1
Download
Related article
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI