$ZrO_2$를 피복한 NiO 분말의 제조 및 미세구조
문지웅, 이홍림, 김구대1, 김재동, 이동아1, 이해원1
연세대학교 세라믹공학과
1한국과학기술연구원 세라믹공정연구센터
Preparation of Zirconia-Coated NiO Powder and its Microstructure
Zirconia coated NiO powders were prepared by the thermal hydrolysis of $Zro(NO_3)_2$.$6H_2O$ in a mixed solvent of alcohol and water. Amorphous zirconium hydroxide was uniformly coated on the surface of NiO powder with the thickness of 20nm. The $ZrO_2$ coating layer was crystallized to tetragonal $ZrO_2$ with the size of 40-60nm at $900^{circ}C$. The coated NiO powder containing 15 vol% $ZrO_2$ was found to have a similar isoelectric point to that of the $ZrO_2$ The grain growth inhibition effect of the coated powders was superior to the mechanically mixed powders.
Key words: Cpated-powder, NiO, Grain growth inhibition, Surface coating
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI