Synthesis and Application of $CeO_2-Sm_2O_3$ Solid Electrolyte Membranes with Electronic and Ionic Conductivities
The oxygen flux of SDC ($Sm_2O_3;doped;CeO_2$) solid electrolyte membranes with electronic and oxygen ion-ic conductivities has been investigated as a basic research in order to develop the conversion process of na-tural gas to syngas using the ceramic membrane reactor. Tube type membranes(1 mm thickness) were fa-bricated by slip casting of SDC powders prepared by the oxalate coprecipitaion method. Dense oxygen per-meation membranes(0.1 mm thickness) could be synthesized via sintering at $1450^{circ}C$ for 2h and their re-lative density was over 95% The oxygen flux through SDC membranes doped 20mol% $Sm_15$ was about $1.13{times}10^{-5};mol/m_2{cdot}sec$ at low temperature around $800^{circ}C$. In addition the SDC membranes showed a good thermaal stability for a long period of service.
Key words: Oxalate coprecipitation, $Sm_2O_3$ doped $CeO_2$ powder, $CeO_2-Sm_2O_3$ solid electolyte, Mixed conductive membrance, Oxygen permeation membrane
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI