SiC 휘스커 보강 $Al_2$O$_3$-SiC 복합체의 열간특성 |
김윤주, 나용한 |
동신대학교 세라믹공학과 |
Thermal Characteristics of SiC Whisker Reinforced $Al_2$O$_3$-SiC Composite |
|
|
|
|
|
ABSTRACT |
SiC whisker reinforced Al2O3-SiC composite was fabricated by reaction synthesis method whish is cost ef-fective and allows good dispersion of whiskers. Fracture strength at room temperature showed the highest value with 150$0^{circ}C$ reaction temperature because a lot of SiC whiskers was formed. Fracture strength at 135$0^{circ}C$ did not show big differences with reaction temperature due to agglomeration of whiskers and formation of sil-icon oxynitride during hot MO(modulus of rupture) test probably promoting grain boundary sliding. |
Key words:
SiC whisker, Al2O3-SiC composite, Reaction synthesis, Silicon oxynitride, Dispersion of whiskers |
|
|
|