J. Korean Ceram. Soc. > Volume 34(9); 1997 > Article
Journal of the Korean Ceramic Society 1997;34(9): 949.
Clinker 생성반응에 미치는 ZnO의 영향
김홍기, 민경소1, 이경희
명지대학교 무기재료공학과
1한라시멘트(주) 기술연구소
The Effect of ZnO on the Formation Reaction of Clinker
With the increase of ZnO content, burnability of raw materials was improved and the formation of clinker minerals was accellerated. When ZnO was added 1wt%, the clinkering temperature was decreased about 30~5$0^{circ}C$. As an increase of ZnO added, aluminate phase was decreased and ferrite phase was increased. When ZnO was added more than 3.0wt.%, the new phases, such as ZnO.Al2O3 and ZnO.Fe2O3 were formed. In the excess of amount of ZnO added, the decomposition of alite phase was intensed and the lamella structure in belite could not be observed due to the decomposition.
Key words: ZnO, Clinker, Clinkering Reaction, Mineralizer
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI