The Piezoelectric Degradation and Mechanical Properties in PZT Ceramics with $MnO_2$ Addition
ABSTRACT
The aim of this study was to investigate the degradation of piezoelectric properties with compressive cy-clic loading, the change in bending strength before and after poling treatment and fracture strength in MPB depending on the amount of MnO2 addition. The MPB with 0.25 wt.% MnO2 showed the best resistance against the piezoelectric degradation with compressive cyclic loading. Bending strength increased when pol-ing and loading directions are parallel, however decreased when poling and loading directions are per-pendicular each other. Because, during poling treatment, compressive residual stress is generated in the pol-ing direction but tensile residual stress in the perpendicular direction to poling direction.
Key words: $Pb(Zr, Ti)O_3$, Piezoelectric property degradation, Cyclic loading, Mechanical properties, Residual stress, $MnO_2$, addition
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI