MgO와 Al의 테르밋 반응생성물이 첨가된 MgO-C계 내화재료의 용손 기구
최태현, 전병세1
경남대학교 무기재료공학과
1전남대학교 무기재료공학과
Wear Mechanism of MgO-C Refractory with Thermite Reaction Products of MgO and Al
ABSTRACT
Thermite reaction products of MgO and Al were added to MgO-C refractory to improve the properties of corrosion against the attack of slag, oxidation and mechanical spalling. Corrosion rate of MgO-C-MgAl2O4 spinel refractory at the ratio of 3.3(CaO/SiO2) slag was smaller than that of MgO-C and MgO-C-Al refractory. The excellent corrosion resistance of the MgO-C-MgAl2O4 spinel refractory against the slag attack was appeared by Al and MgAl2O4 spinel with high melting point and corrosion resistance and the high thermal conductivity and low thermal expansion of AIN. Hot M.O.R at 140$0^{circ}C$ and the resistance of oxidation weight loss at 90$0^{circ}C$ were 210kg/cm2 and -12% respectively.
Key words: Thermite, MgO-C, Refractory, Corrosion, Spalling
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI