Journal of the Korean Ceramic Society 1996;33(4): 432.
졸-겔법으로 제조한 $ZrO_2$ 의 코발트 흡착량에 미치는 하소온도의 영향
김유환, 김용익, 배성렬1
1한양대학교 화학공학과
Effect of Calcination Temperature on Cobalt Adsorption Capacity of$ZrO_2$ prepared by Sol-Gel Process
ZrO2 gel was prepared under pH 10 alkaline condition by sol-gel process and was investigated as a function of calcination temperature and effect of calcination temperature on cobalt adsorption capacity. The ZrO2 powder prepared by sol-gel process was calcined at 600, 800, 1000, 1200, 140$0^{circ}C$ and analyzed by X-ray diffractometry. SEM specific surface area by BET nitrogen adsorption FT-IR and TG-DTA technique. It was shown that cobalt adsorption capacity of ZrO2 prepared under pH 10 alkaline condition and then calcined at $600^{circ}C$ in high temperature was determined to be larger than that of ZrO2 at various calcination temperature. The specific surface area of ZrO2 calcined at $600^{circ}C$ was 24.03m2/g and cobalt adsorption capacity at 25$0^{circ}C$ high-temperature water was 0.16m-eq/g
Key words: Zirconia, Monoclinc, Tetragonal, Sol-gel, Cobalt adsorption
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI