FEM Residual Stress Analysis and Mechanical Properties of Silicon Nitride/Stainless Steel Joint with Multi-Interlayer
ABSTRACT
The thermal residual stresses were estimated for brazed Si3N4/S.S.316 joints with Cu/Mo multi-interlayers using FEM, and their bending strengths at room temperature were measured for various interlayer configura-tions. The Cu, Mo multi-interlayer decreased the maximum residual stress in Si3N4 and caused the residual stress redistribution rsulting in the high residual stress at Mo interlayer. The stress distribution in the joints as well as the maximum residual stress in silicon nitride were found to be main factors for determining bending strengths and Weibull modulous of the joints. The bending strength of the brazed Si3N4/S.S.316 joints with specific Cu, Mo multi-interlayer system were found to be above 400 MPa.
Key words: Ceramic-metal joining, Brazxing, Residual stress, Joint strength, Multi-interlayer
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI