 플라즈마사용법에 의한 $ZrO_2-Y_2O_3$ 코팅의 고온에서의 마모 김장엽, 임대순, 안효석1 고려대학교 재료공학과1한국과학기술원 Tribology 연구실 High Temperature Wear of Plasma-Sprayed $ZrO_2-Y_2O_3$ Coatings ABSTRACT The sliding wear behavior of the plasma sprayed zirconia containing 8wt% yttria was investigated over a range of room temperature to 800℃. Both of the friction coefficient and the wear loss increased reaching its maximum at about to 499℃. and then decreased again with increasing temperature up to 800℃. The worn surface at elevated temperature were observed and analyzed by scanning electron microscopy and X-ray diffractometer to study the mechanisms of high temperature wear behavior. Surface morphology of the worn samples changes with temperature. Monoclinic (m)/tetragonal (t) x-ray peak intensity ratio of wear debris and worn surface decreased with increasing temperature. Non-transformable tetragonal (t') to metastable tetragonal (t) phase transformation of worn surface increased with increasing temperature. The results indicate that dehumidification and above phase changes are contributing to the high temperature wear behavior of the plasma sprayed ZrO2-Y2O3 coatings.
TOOLS
Full text via DOI
 Related articles Study on High-Temperature Oxidation Behaviors of Plasma-Sprayed TiB2-Co Composite Coatings  2018 March;55(2) Preparation of Nanotube-shaped $TiO_2$ Powder  2000 ;37(7) Sintering and the Electrical Properties of Co-doped $ZnO-Bi_2O_3-Sb_2O_3$ Varistor System  2000 ;37(2) High-Temperature Degradation of Hot-Pressed $t-ZrO_2$ Co-doped with $Y_2O_3$ and $Nb_2O_5$  1997 ;34(9) Low Temperature Degradation Behavior of $^{18}O$-Containing Y-TZP  1997 ;34(2)