저온소결 세라믹기판용 Cordierite계 결정화 유리의 합성 및 특성조사에 관한 연구;(III) Tape casting에 의한 기판 제조
김병호, 문성훈, 이근헌, 임대순
고려대학교 재료공학과
Synthesis and Characterization of Cordierite Glass-Ceramics for Low Firing Temperature Substrate; (III) Fabrication of substrates by tape casting process
Low firing temperature substrate were synthesized through tape casting and sintering of glass with cordierite composition and then their properties were investigated. Even though the dielectric properties and XRD patterns of substrates, obtained by tape casting and sintering at 900~100$0^{circ}C$ for various periods, were similar to those of substrates obtained by dry pressing, the sinterability was enhanced. The substrates were thin and the size was 0.6$times$50$times$50mm. From the results of dielectric properties, the sinterability and X-ray diffraction pattern, the proper condition for cofiring process with conductor, Cu, was 90$0^{circ}C$ for 1h. The properties of the substrate are as follows; the dielectric constant was 5.31(at 1MHz), the dissipation factor was 0.0028, the apparent porosity was 0.28% and the main crystalline phase was $alpha$-cordierite.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI