Journal of the Korean Ceramic Society 1993;30(7): 557.
Raw Coke 전처리 온도에 따른 경질 탄소재의 물성 영향
황인수, 염희남1, 장진석2, 이종민2, 송종택
단국대학교 재료공학과
1명지대학교 무기재료공학과
2요업기술원
Influence of Properties on Carbon Solid by Preheat-treatment Temperature
ABSTRACT
Following conclusions are made from the detalied research on the relation between the phase change of the petroleum raw cokes after ball milling and the preheat treatment temperature. The petroleum raw cokes species are preheated in the temperature range of 350~45$0^{circ}C$. At the preheat treatment temperature of 40$0^{circ}C$ the particles of petroleum raw cokes from ball milling become spheically shape with the almost uniform particle size distribution of 1~5${mu}{textrm}{m}$. At the same temperature, they became low-graphitized with the d0.02 X-ray diffraction index of 3.41$AA$. The carbon material made from the petroleum raw cokes at 40$0^{circ}C$ turned out to have the good modulus of rupture about 600kg/$textrm{cm}^2$, with the bulk density around 1.8g/㎤ and the appearent porosity around 8%.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI