 $Li_2O-B_2O_3-P_2O_5$계 유리의 이온전도성 박강석, 강은태 경상대학교 무기재료공학과 Ionic Conductivity of $Li_2O-B_2O_3-P_2O_5$ based Glasses ABSTRACT Li2O-B2O3-P2O5 glasses with high lithium content were analysed by electrical characterization. The electrical conductivity increase with Li content and exhibits a maximum value of 1.2$times$10-4S/cm near B2O3/P2O5=1 at 15$0^{circ}C$. Glass transitiion temperature increased with conductivity. Concentration of charge carrier and distribution of relaxation time were independent of temperature. In this system the variation of conductivity with the composition was depend on mobility of lithium ion. Basically, it is attribute to primitive activation energy. Enhancement of conductivities was related to be formation of (B-O-P)-, di-, and metaborate group, which give additional available sites for Li+ diffusion.
TOOLS
Full text via DOI
 Related articles Electrical Conductivity of ${La_{2-x}}{Sr_x}{Mo_{2-y}}{Cr_y}{O_{9-\delta}}$Ionic Conductors  2001 ;38(8) Electrical Conductivity of Sr-doped $ErCrO_3$Solid Solutions  2000 ;37(12) Electrical Conductivity of YO$_{1.5}$-TaO$_{2.5}$-MgO Based Fluorite Phase  1998 ;35(5) Effect of Modifiers on the Electrical Resistivity of $SiO_2-Al_2O_3-B_2O_3-RO-Na_2O$ Glasses  1996 ;33(4) Lithium Ion Conductivity in $Li_{3x}La_{(2/3-x)}TiO_3$ system  1996 ;33(3)