습식합성에 의한 Mn-Zn Ferrite의 생성반응에 관한 연구
이경희, 이병하, 허원도1, 황우연1
명지대학교 공과대학 무기재료과
Formation Reaction of Mn-Zn Ferrite by Wet Process
Formation reaction of Mn-Zn ferrite depending on various synthetic conditions of wet process was investigated using FeCl2.nH2O(n≒4), MnCl2.4H2O, ZnCl2 as starting materials. A stable intermediate precipitate was formed by the addition of H2O2. And the precipitate was hard to transform to spinel phase of Mn-Zn Fe2O4. Single phase of Mn-Zn Fe2O4 spinel was obtained above 8$0^{circ}C$ reaction temperature. The powder had spherical particle shape and 0.02~0.05${mu}{textrm}{m}$ particle size. Fe(OH)2 solid solution, -FeO(OH) solid solution, -FeOOH, Mn-Zn Fe2O4 spinel were formed with air flow rate 180$ell$/hr. However, single phase of Mn-Zn Fe2O4 spinel with cubic particle shape and 0.1~0.2${mu}{textrm}{m}$ particle size was formed with synthetic conditions of 8$0^{circ}C$ and 90 munutes. The particle shape of the -FeOOH was needle-like.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI