J. Korean Ceram. Soc. > Volume 27(3); 1990 > Article
Journal of the Korean Ceramic Society 1990;27(3): 299.
YBCO 고온 초전도체 후막의 제작 및 특성 연구
정형진, 박홍순1, 이전국, 송진태1
한국과학기술연구원 세라믹스부
1한양대학교 재료공학과
Fabrication and Characterization of High $T_c$ $YBa_2Cu_3O_7-x$ Thick Films
ABSTRACT
The fabrication of Y-Ba-Cu-O films and experimental factors affecting to characteristics of films are studied in detail. Superconducting thick films are fabricated by the screen printing method. The metal-citrate precursors are obtained simply by mixing of metal nitrate with citric acid. The particle size of heat treated powders is approximately 0.3-1${mu}{textrm}{m}$ and the thickness of film is estimated as 30-35${mu}{textrm}{m}$. According to the XRD analysis, the films sintered at 870-93$0^{circ}C$ for 10min. -6hr with P(oxygen)=1atm has the unique orthorhombic crystal symmetry indicating the 123 phae. Tc, onset is determined around 92-87。K, but it shows semiconducting behavior probably due to the oxygen deficiency in the lattice, porosity and impurities in films. Extrapolated Tc, zero is estimated as 76-50。K. For films sintered at 90$0^{circ}C$ for 1hr, superconducting properties are observed with the room temperature resistivity of 0.025$Omega$.cm Tc, onset at 88。K and Tc, zero at 63。K.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI