SHS법에 의한 TiC의 합성 및 소결특성
이형복, 정윤중, 여철현1, 김관일
명지대학교 무기재료공학과
1연세대학교 화학과
Systhesis and Sintering Characterization of TiC by Self-Propagating High Temperature Synthesis
Titanium Cabride powders were prepared by the self-propagating high temperature synthesismethod in air from the mixture of metal titanium powder and carbon powder. The result are as follows : 1. The conversion effciency of higher than 95% can be obtained and the lattice constant value of the product was 4.322$AA$. 2. The combustion mode, velocity and temperature of combustion wave was photographed using high-speed camera, and showed steady-state, velocity of 15.414mm/sec at 250$0^{circ}C$. 3. The relative density and MOR strength of TiC sintered at 180$0^{circ}C$ for 90 minutes by hot-pressing under the pressure of 200kg/$textrm{cm}^2$ were 95% and 395MPa, respectively.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI