CeO2 안정화 정방정 Zirconia 다결정체(Ce-TZP)에 관한 연구(II) : Ce-TZP의 고온 기계적 성질과 파괴거동의 변화
강대석, 김문일, 박정현1, 문성환1, 백승수2
연세대학교 금속공학과
1연세대학교 요업공학과
2국방 과학 연구소
A Study on the Ceria Stabilized Tetragonal Zirconia Polycrystals(Ce-TZP)(II) : Mechanical Properties of Ce-TZP and its Fracture Behavior at Elevated Temperature
ABSTRACT
The high-temperature strength of Ce-TZP was measured at 200, 650 and 100$0^{circ}C$ by 4-point bending test. And its fracture behavior was observed by SEM. Below $650^{circ}C$ of the temperature, where monoclinic fraction was almost zero, the decreasing rate of bending strength was relatively slow, but above this temperature, high temperature strength was largely decreased as a result of the decrease of stress-induced transformation of zirconia. The observation of fracture surface bended at 100$0^{circ}C$ indicated that the fracture mode changed from intergranular-into transgranular-form with regardless of ceria contents.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI