공침법으로 제조한 ZrO2-MgO계 분말특성
이형복, 정윤중, 김영규, 이홍림1
명지대학교 무기재료공학과
1연세대학교 요업공학과
Powder Properties of ZrO2-MgO System Prepared by Co-precipitation Method
The properties of the powders of ZrO2-MgO system prepared by co-precipitation method using ZrOCl2.8H2O and MgCl2.6H2O as starting materials were investigated after calcination from $600^{circ}C$ to 120$0^{circ}C$. The crystallization temperature of amorphous ZrO2 was increased as MgO contents increased. The crystallite size of ZrO2 was increased with increasing calcination temperature. The crystallite size of tetragonal ZrO2 calcined at 100$0^{circ}C$ for 1hr wa about 45nm, and MgO contributed effectively to promoting stability of tetragonal Zirconia.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society. All rights reserved.                      Developed in M2PI