Ethyl Silicate를 고순도 $beta$-SiC미분말 합성에 관한 연구(I) 반응조건과 $beta$-SiC의 생성율 및 특성
최용식, 박금철1
국립공업시험원 도자기시험소
1한양대학교 공과대학 무기재료공학과
A Study on Synthesis of High Purity $beta$-SiC Fine Particle from Ethylsilicate(I) -Reaction Conditon, Yeild and Properties of $beta$-SiC-
In order to obtain the high purity $beta$-SiC powder that possesses the excellent sinterability and is close to the spherical shape, the carbon black was mixed into the composition of Si(OC2H5)4-H2O-NH3-C2H5OH which the monodispersed spherical fine particles is formed the hydrolysis of Ethylsilicate and the mixture was carbonized under an argon atmosphere. Particle shpae, size and the yield of $beta$-SiC powder were investigated according to the molar ratio of carbon/alkoxide and variations of reaction temperature and reaction time. The results of this study are as follow ; 1) The yield of $beta$-SiC gained from the reaction for one hour at 150$0^{circ}C$ almost got near 100% and the particle size of $beta$-SiC from the reaction for 15 hrs at 150$0^{circ}C$ was 0.2${mu}{textrm}{m}$ on the average and close to the spherical shape agglomerate state. 2) When the molar ratio carbon/alkoxide is over 3.1 and the reaction occurs at 145$0^{circ}C$ for 5hrs, the carbon content has not an effect on the kind of crystal of product.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI