종결정법을 이용한 저전압 ZnO 배리스터의 제조 및 전기적 특성
강승구, 오재희
인하대학교 무기재료 공학과
Preparation of Low Voltage ZnO Varistor Using Seed Grain Method and Its Electrical Properties
ZnO low voltage varistor was obtained by varying a) the amount of seed grains, b) the size of seed grains, and c) sintering temperature. Also, the optimum condition for fabricating the ZnO seed grains was studied. Large ZnO seed grains were obtained by washing a ZnO sintered body containing 1m/of BaCO3 in boiling water. When the seed grains were added, abnormal grain growth occurred, and the varistor voltage sharply decreased. However, when more than 5w/o of seed grain content was added, the varistor voltage gradually increased. When 10w/o seed grains of 75~106${mu}{textrm}{m}$ were added and sintered for 2 hours at 1200 to 125$0^{circ}C$, low voltage varistor properties with V1mA/mm of 19V/mm and nonlinear exponent ($alpha$) of 12 occurred.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI