Journal of the Korean Ceramic Society 1987;24(3): 215.
운모표면에 대한 $alpha$산화철 흡착
김대웅, 조동희1, 김명숙2, 박면용2
고려화학(주) 연구소
1한국섬유공사 시험소
2건국대학교 화학과
Adsorption of $alpha$-Fe2O3 on the Surface of Mica Particles
${alpha}$-Ferric Hydrous Oxide and ${alpha}$-Ferric Oxide were obtained as following processes that Ferric Nitrate solution was adjusted to pH 6-8 with Ammonium Hydroxide, refluxed the Iron precipitate for 1 hr. at 80$^{circ}C$, washed it with water and Methanol (95%), dried it to obtain ${alpha}$-Ferric Hydrous Oxide at 60$^{circ}C$, and then heated in atmosphere to prepare ${alpha}$-Ferric Oxide for 1 hr. at 450$^{circ}C$. Mica particles cleaned with ultrasonicator (45KHz) in water were mixed with Ferric Nitrate solution and treated it to adsorb ${alpha}$-Ferric Oxide on the surface of mica particles by using the abovementioned processes, but the heated temperature was at 500$^{circ}C$. The maximum wavelength of reflected light on the surface of mica-${alpha}$-Ferric Oxide (50%) was appeared at 546nm but -Ferric Oxide free mica only was at 436 nm. The maximum wavelength was shifted to longer when the weight ratios of ${alpha}$-Ferric Oxide to mica was changed from 1% to 50%.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI