J. Korean Ceram. Soc. > Volume 19(4); 1982 > Article
 Journal of the Korean Ceramic Society 1982;19(4): 275.
 $CaO-Al_2O_3-SiO_2$ 계의 열간반응에 관한 연구 백용혁, 이종근 한양대 무기재료공학과 A Study on Reaction of During Firing of $CaO-Al_2O_3-SiO_2$ System ABSTRACT This study was carried out to research the change of mineral phases and the characteristics (apparent specific gravity, water absorption, firing shrinkage and thermal expansion etc) of the sintered bodies composed of larnite, wollastonite and anorthite etc. in $CaO-Al_2O_3-SiO_2$ system. Test bodies were composed of the same theoretical composition as it of anorthite and fired up to $1450^{circ}C$. Investigated the change and micro-structure of the mineral phases by XRD and SEM, the characteristics of the sintered bodies by DTA/TGA and etc. The results were as follows. 1. The sintering temperature had a higher about $60^{circ}C$ than that of $CaO-SiO_2$ system because of coexisting $Al_2O_3$. 2. The formation and transition temperature of $beta$-wol lastonite and $alpha$-wollastonite were similar to the results of $CaO-SiO_2$ system. 3. The formed larnite and wollastonite were decomposed and melted at about $1260^{circ}C$. 4. Anorthite began to be synthesized at $1140^{circ}C$, its quantity was repidly increased according to the temperature rising.
TOOLS
Full text via DOI
 Related articles Microstructural Development During Microwave Sintering of CaO-$ZrO_2$-$SiO_2$Glass  2000 ;37(12) A Study on the Saturation of Grain Size in Pb(Zr, Ti)$O_3$ Thin Films  2000 ;37(6) Sintering and the Electrical Properties of Co-doped $ZnO-Bi_2O_3-Sb_2O_3$ Varistor System  2000 ;37(2) A Study on the Crystal Structure of $SrNd_2Ti_4O_12$  1999 ;36(11) Refractive Index Dispersion of Aluminate Glasses on the Addition of $SiO_2$  1997 ;34(7)