탄화규소-점토-Kaolin Chamotte 계의 소결에 미치는 첨가제 $Al_2O_3$의 영향
백용혁, 박종훈1
전남대 공대
Effect of $Al_2O_3$ as Additives on the Sintering of Sic-Clay-Kaolin Chomotte System
The sintering characteristics of the SiC-Clay-Kaolin chamotte system were studied by addition of $Al_2O_3$ for the manufacture of silicate-bonded silicon carbide refractories at $1350^{circ}C$. The sinterbilit of SiC-Binder mixture was measured by apparent porosity and compressive strength. And its mineral compositions were identified with X-ray diffractometer. The following results were obtained; 1) Optimum amount of mixed clay ($textrm{Al}_2textrm{O}_3$ 40 wt% mixed) as a binder was about 25wt% 2) Appropriate mixing ratio of mixed Kaolin chamotte ($textrm{Al}_2textrm{O}_3$ 40wt% mixed) was about 30wt% in the clay Kaolin chamotte binder. 3) Variation of apparent porosity and compressive strength of sintered SiC-binder mixture fired at $1350^{circ}C$ were due to the sinterbility of clay.
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI