Phase Relations and Microstructure of Comounds in the $Si_3N_4-Al_2O_3-SiO_2$ system at $1700^{cire}C$ |
|
|
|
|
|
ABSTRACT |
The phase relations and microstructure appeared at 1700℃ in a system of Si3N4-Al2O3-SiO2 were studied. The samples were pressurelessly sintered at 1700℃ for 1hr and reheated at 1600℃ for 1hr under nitrogen atmosphere. The compounds formed were identified by X-ray diffraction method and the microstrues were observed by SEM. The stable phases appeared in this system were X-phase, Si2ON2, β'-Si3N4 and Mullite. From the results of those experiments, it was concluded that the X-phase has very close composition to that proposed by G, K. Layden, Si3Al6O12N2. SEM photographs showed that Si2ON2 was a plate phase and X-phase was a rectagular plate phase. |
|
|
|