Jung and Chung: Absence of Distinctively High Grain-Boundary Impedance in Polycrystalline Cubic Bismuth Oxide


In this work, we studied a fluorite structure oxides: Yttria stabilized zirconia, (YSZ); Gd doped CeO2 (GDC); erbia stabilized Bi2O3 (ESB); Zr doped erbia stabilized Bi2O3 (ZESB); Ca doped erbia stabilized Bi2O3 (CESB) in the temperature range of 250 to 600°C using electrochemical impedance spectroscopy (EIS). As is well known, grain boundary blocking effect was observed in YSZ and GDC. However, there is no grain boundary effect on ESB, ZESB, and CESB. The Nyquist plots of these materials exhibit a single arc at low temperature. This means that there is no space charge effect on δ-Bi2O3. In addition, impedance data were analyzed by using the brick layer model. We indirectly demonstrate that grain boundary ionic conductivity is similar to or even higher than bulk ionic conductivity on cubic bismuth oxide.

1. Introduction

δ-Bi2O3 is drawing much attention as the most well-known material among oxygen ionic conductors.1-5) The attention is due to the high ionic conductivity of δ-Bi2O3. The ionic conductivity of δ-Bi2O3 is higher than that of yttria stabilized zirconia (YSZ) (5 × 10−3 S/cm at 600°C), which is frequently used as an oxygen ionic conductor, by two orders of magnitude and is higher than that of gadolinium doped ceria (GDC) (2.5 × 10−2 S/cm at 600°C) by one order of magnitude. 6-7) The high ionic conductivity of δ-Bi2O3 is due to the oxygen vacancy concentration (25%) and the anion mobility in δ-Bi2O3 which values are higher than those of acceptor-doped ceria or acceptor-doped zirconia having the same fluorite-type structure (Fig. 1).8) However, the overall ionic conductivity of actual polycrystals is determined by not only the bulk ionic conductivity but also the ionic conductivity of the grain boundaries. According to Guo,9) in acceptor-doped zirconia and acceptor-doped ceria, which are materials having a fluorite-type structure like that of δ-Bi2O3, the ionic conductivity at the grain boundaries is several orders of magnitude lower than the bulk ionic conductivity, which is called the grain boundary blocking effect.10-14) These two factors are often mentioned as the causes of the grain boundary blocking effect. First, grain boundary siliceous phases impede ionic conduction.13-14) However, the grain boundary blocking effect is even found in high-purity materials.12-15) This blocking nature can be accounted by the presence of a space charge layer near the grain boundary core.12,16-17) Many experiment results support a role of space charge. Lei used transmission electron microscopy (TEM) and electron energy loss spectroscopy (EELS) to determine an increase of oxygen vacancy and Y segregation at the grain boundary core of YSZ and also demonstrated that Gd segregation and oxygen vacancy were higher at the grain boundaries than in the bulk GDC.18) Lee directly observed the Gd segregation and high concentration of oxygen vacancy near grain boundaries using scanning transmission electron microscopy-X-ray spectroscopy (STEM-EDS). In addition, in this work, Kelvin probe force microscopy (KFM) verified Grain boundary is positively charged and the potential difference between grain boundary and bulk. Moreover, the potential difference was equal to the calculated data from impedance analysis applying the Schottky barrier model.19) However, same fluorite-type structure δ-Bi2O3 didn’t show grain boundary effect.20) In this work we added an aliovalent dopant to δ-Bi2O3, as it was done in YSZ and GDC to know whether grain boundary effect shows or not. The difference of the ionic radius makes an elastic filed and it causes the segregation in the grain boundary.21) So we selected a dopant which has a small ionic radius difference with Bi2O3 (r[Bi3] = 1.17 Å)22) to exclude the segregation effect as much as possible. A tetravalent donor ZrO2 (r[Zr4+ = 0.84 Å])22) and a divalent acceptor CaO (r[Ca2+ = 1.12 Å])22) were doped to Bi2O3 to investigate the grain boundary blocking effect caused by the space charge layer. Using Kröger-Vink notation, 23) we describe a doping Bi2O3 with donor and acceptor, as follows:
Doping with the donor Zr was expected to lead to a positively charged space charge layer because of ZrBi· segregation at the grain boundary (Eq. 1a), while the doping with the acceptor Ca was expected to generate a negatively charged space charge layer because of the CaBi segregation at the grain boundary (Eq. 1b). Since δ-Bi2O3 is converted to α-Bi2O3 at 723°C,24) for stabilization at room temperature, we doped δ-Bi2O3 with 20 mol% Er. We call this erbia-stabilized bismuth (ESB), Bi0.8Er0.2O1.5. In addition, 2 mol% Ca and 5 mol% Zr were doped into the ESB. Polycrystal 8 mol% Y doped ZrO2, single-crystal 8 mol% Y doped ZrO2, and 10 mol% Gd doped CeO2, which also have fluorite structure were used for comparison. In addition, we perform X-ray diffraction (XRD) analysis to identify synthesized materials. Microstructures of the samples were analyzed by scanning electron microscopy (SEM) to verify the absence of a secondary phase at the grain boundary. The ionic conductivity of the bulk and the grain boundaries is measured with the electrochemical impedance spectroscopy.

2. Experimental Procedure

Bi0.8Er0.2O1.5 (ESB) was synthesized by conventional solid-state synthesis using Bi2O3 (99.8%, Aldrich) and Er2O3 (99.99%, Aldrich) powders. The powders were Ball-milled for 24 h using zirconia balls, and then the powders were sieved using a 300 mesh sieve. Subsequently, the resulting powders were calcinated at 800°C for 10 h. The (Bi0.8Er0.2O1.5)0.95-(ZrO2)0.05 (ZESB) powder doped with 5 mol % Zr was synthesized by the same method using Zr2O3 (99.99%, Aldrich) powder as a dopant. (Bi0.8Er0.2O1.5)0.98(CaO)0.02 (CESB) powder doped with 2 mol % Ca was synthesized by the same method using CaCO3 (99.99%, Aldrich) as a dopant. X-ray diffraction (XRD, RIGAKU D/MAX-2500) was used to verify if the powders were well synthesized, and X-ray diffraction pattern analysis in the 2θ range from 20° to 80° was obtained using CuKα1CuKα = 1.5406 Å at room temperature. Pellets having a diameter of 10 mm were prepared by using a calcinated powder. The pellet were uniaxial pressed using Cold isostatic pressing (CIP) at 200 MPa. Then the pellet was sintered in air at 890°C for 16 h. Ce0.9Gd0.1O1,95 (GDC) powder was purchased from Aldrich. Pellets having a diameter of 10 mm were prepared by using a GDC powder. The pellet were uniaxial pressed using CIP at 200 MPa. and the sample was sintered at 1500°C for 12 h. 8 mol% Y doped ZrO2 (YSZ) polycrystalline substrate with a size of 1 cm × 1 cm × 0.5 cm and a 8 mol% Y doped ZrO2 (YSZ) single-crystal [100] substrate with a size of 1 cm × 1 cm × 0.5 cm were used; both were purchased from MTI KOREA. To measure the impedance spectra, Pt paste was applied on both sides of the pellets, and then samples were sintered at 800°C for 2 h in air to make electrodes. The ionic conductivity of the samples was measured by using an EIS (VSP-300, Biologic) over a frequency range of 1 Hz to 5 MHz with a voltage amplitude of 50 mV. The measurement data were analyzed using the EC-Lab software program (ver. 11.02). For the analysis of the microstructure, all samples were thermally etched at 800°C for one minute and GDC were thermally etched at 1300°C for one minute, and the microstructures were observed using SEM (Hitachi SU5000).

3. Results and Discussion

3.1 Microstructural and structural characterization

A cubic crystal structure (space group of Fm-3m) δ-Bi2O3 has a stable phase from 723°C to 825°C, the melting point.24) On cooling below 723°C, δ-Bi2O3 is transformed to monoclinic Bi2O3. Doping the cubic δ-Bi2O3 with cations with high polarizability is known as an effective method of stabilizing the cubic δ-Bi2O3 phase. Among the high polarizability cations, Er has a relatively small ionic radius and can stabilize δ-Bi2O3 with a minimum amount of dopant. Doping δ-Bi2O3 with 20 mol% Er is the optimal doping concentration and showed the highest ionic conductivity.25) In this work, ESB was doped with 2 mol % Ca. this is not at the same concentration of the zirconia dopant, 5 mol%. Because the solubility of Ca in ESB is lower than 5 mol%. XRD was performed to characterize the ESB, CESB, and ZESB powders calcinated at 800°C for 10 h. The XRD data showed that all the peaks of the ESB, CESB, and ZESB powders were well matched with the peak of δ-Bi2O3, which had a cubic crystal structure (ICDD card 00-034-0377; a=5.479 A) (Fig. 2). A small amount of γ-Bi2O3, formed from slow cooling of δ-Bi2O3, was detected in the ZESB and CESB powders; no other secondary phase was found. Size of the grains can be obtained from the cross-sectional SEM images; the images showed no secondary phase at the grain boundaries (Fig. 3). In addition, the SEM images also confirmed that the singlecrystal YSZ has only one grain without a grain boundary, and confirmed that all the samples were sintered densely.

3.2. Brick layer model

Electrochemical Impedance spectroscopy is a very useful measurement method because the conductivity of the bulk and the grain boundaries can be separately measured in a polycrystalline material. In this study, the brick layer model was applied for impedance spectra analysis27-29) The description of the brick layer model is given a review article by Haile.27) Fig. 4 shows the general circuit and a typical Nyquist plot of polycrystals. The Nyquist plot is a plot in which the x-axis represents the real part of the impedance and the y-axis is the imaginary part of the impedance. The circuit consists of three RQ sub-circuits, wherein R (ZR = R) denotes the resistance and Q the constant phase element (CPE). ZQ = [Y( jwn)]−1, wherein j=-1, ω is the frequency, Y and n are constants, and n is a value between 0 and 1. If n, which experimentally determines the characteristics of the RQ sub-circuits, is close to 1, the constant phase elements is similar to a capacitor, and Y is called the pseudocapacitance. The frequency at the vertex of the semicircle shown in Fig. 4 is referred to as the characteristic frequency, w0, of the sub-circuit RQ, which is expressed as (YR)−1/n. If the frequency of that circuit is sufficiently different from another and n is close to 1, the resistance of each circuit can be calculated from the size of the arc on the real axis, and the capacitance of the sub-circuit is given as (Rw0)−1. The resistance values are R1 and R2 of the RQ circuit. To associate these values with physical meanings, a cubic grain boundary model was assumed, wherein the model includes grain boundaries that are parallel or vertical to the applied field (Fig. 5).27) In Fig. 5, L denotes the length of the sample, A the cross-sectional area of the sample, d the edge length of a grain, and δ the thickness of the grain boundary. If δ << d, the total length and the area of all samples for all the perpendicular (or series) grain boundaries is given by: L = (δ/d)L and A = A. Similarly, the total length and the area of all the parallel grain boundaries is given as L|| = L and A|| = (2δ/d)A. Fig. 6 shows the RQ sub-circuit corresponding to an ideal polycrystalline material. The first (RQ) circuit consists of parallel grain boundaries and grain interiors, and the second RQ circuit consists of the only series grain boundaries. The third CPE represents the electrode reaction. The equivalent circuit of Fig. 6(a) can be simplified, as done in Fig. 6(b) by combining the two parallel resistances into one simple resistance. Similarly, two CPEs can be merged into one Q. If the value of n is assumed to be the same, the entire pseudo-capacitance may be expressed as Ygb|| = Ybulk (Fig. 6(b)). In addition, as is known empirically, it was assumed that the low to mid frequency arc is related to the responses of grain boundaries in series with grain interior and the high frequency arc corresponds to the combined the response of grain interiors and parallel grain boundaries. Taking the specific conductivities of the grain boundary and the bulk are σgb and σbulk, respectively, and if the conduction in series and parallel grain boundaries follows the same mechanism, yield
Defining σi=L/A{1Ri}, Eqs. (2) and (3) may be rewritten as follows:
From an impedance measurement and an information of the macroscopic sample dimensions, R1 and R2 can be obtained at once from the Nyquist plot, but σgb and σbulk cannot be obtained. However, the impact of the relative magnitudes σgb and σbulk on the relative magnitudes of R1 and R2 can be handled easily under various limiting conditions. The ratio of R1 to R2 can be obtained from the ratio between σ1 and σ2.
As shown by the relation above, the ratio of R1 and R2 is related to both (σbulkgb) and (δ/d).

Case (1): σbulk > σgb

For the situation where σbulk > σgb, the material generally has a microstructure with δ << d. Therefore, Eq. (6) is reduced to:
Similarly, Eq. (4) is reduced to:
Equation (8) is general assumption for impedance analysis to calculate bulk conductivity. The Nyquist plots of materials with σbulk > σgb will present two distinguishable arc. if 1) R1 and R2 are comparable in magnitude, and 2) the characteristic frequencies of the two domains are sufficiently different. Materials with typical microstructure (δ/d < 1 and σbulk > σgb > 1), will have 0.01 < R1 < R2 < 100. Therefore, the first condition is met. The characteristic frequency of a material or a material domain is given by w0 = 1/RC, wherein w0 is a unique characteristic of a material that is independent to the geometric factors. Alternatively, w0 can be expressed as 1/ρɛɛ0, wherein ρ is a resistivity given by 1/σ, ɛ denotes the relative permittivity, and ɛ0 denotes the vacuum permittivity. Therefore, the question whether w0,bulk is significantly different from w0,gb or not is eventually turned to whether (ρgbɛgb) is significantly different from (ρbulkɛbulk) or not. While resistivities of materials cover many orders of magnitude, dielectric constant do not significantly changed. Hence, ɛbulk ~ ɛgb is a reasonable assumption. Therefore, the question is reduced to whether ρbulk is significantly different from ρgb or not. Since σbulk > σgb is first assumed, by definition ρgb > ρbulk, which eventually implies w0,bulk > w0,gb. Consequently, two arc will be presented in the Nyquist plot, and the semicircle at the low frequency will correspond to the responses of grain boundaries. More specifically, the characteristic frequency of the high frequency arc is determined as a combined the dielectric response of the grain interiors and parallel grain boundaries. However, since the parallel grain boundaries have an unfavorable geometric structure (a small area, and a long length), their contribution of the parallel grain boundary to the capacitance is negligible. In a typical microstructure, if σbulk > σgb, σbulk may be immediately obtained (Eq. 8). However, σgb requires the information about the grain size and the grain boundary (Eq. 5). In absence of microstructural observations, only d/δ can be directly estimated. Each RQ sub-circuit has a capacitance value. It can be obtained from the resistance and the characteristic frequency, and the two variables, Y and n of CPE which characterize the constant phase element. Specifically,
As mentioned above, due to the unfavorable geometry of the parallel grain boundary, the dielectric constant C1 is related to the high frequency arc and it is entirely associated to the bulk. On the contrary, C2 is related to the low frequency arc and it is almost exclusively associated to the vertical (or series) grain boundary. Therefore, C1 and C2 may be expressed as in the following equations:
Since the overall dielectric characteristic of the bulk and the grain boundary is quite similar (ɛbulk ~ ɛgb),
Therefore, both the specific grain interior conductivity and the specific grain boundary conductivity can be measured by accurately using the relevant variables without microstructural observations.

Case (2): σgb > σbulk

In this case, for those materials which have typical microstructures, δ/d no greater than 1/100, no simplification to Eq. (6) can be applied. Eq. (2) is applied to determine the shape of the Nyquist plot in the following three different sub-cases:

(a) σgb/σbulk>>d2δ(Rgb<<Rbulk)

In this sub-case, Rgb|| becomes dominant over R1; the ionic transport along the parallel grain boundary is preferred to the passage through the grain interiors

(b) σgb/σbulk~d2δ(Rgb~Rbulk)

In this sub-case, Rgb|| since is similar to Rbulk, the ionic transport occurs through both the parallel grain boundary and the grain interiors.

(c) σgb/σbulk<<d2δ(Rgb>>Rbulk)

The resistance R1 will be dominated by Rbulk. Therefore, the assumptions for Eqs. (7) and (8) are valid. As assumed above, if the dielectric constants of bulk is similar to that of grain boundaries and n is close to 1, the capacitance of the first RQ sub-circuit (Fig. 6(b)) may again be expressed as C1 ~ Cbulk in all the sub-cases. In the sub-cases (a) and (b), R1 is within a factor of two Rgb||. However, in sub-case (c), R1 is close to Rbulk. In all the sub-cases, the second RQ circuit resistance, R2, is much smaller than R1. In sub-cases (a) and (b), R2 may be expressed as in the following equation:
On the other hand, in sub-case (c), R2 may be expressed as in Eq. (7). In all the sub-cases, the capacitance of the second RQ circuit may be expressed as in the following equation:
The final approximation was based on Eq. (12). Since the responses of the first and the second sub-circuits are different, in the case of σgb > σbulk, the Nyquist plot theoretically exhibit two arcs. In contrast to what is generally observed results, the high frequency arc corresponds to the R2Q2 sub-circuit of the grain boundary in series with (or perpendicular to) grains, while low frequency arc corresponds to the combined R1Q1 sub-circuit of the parallel grain boundaries and grain interiors. This is the result of R2C2 < R1C1 (Eqs. (4), (10), and (11)). However, a two arcs spectrum is not actually be obtained, because the radius of the high frequency arc, R2, is several orders of smaller than low frequency arc. For example, if σgbσbulk<<d2δ and δ/d = 1/100, R2/R1 = 10−4. Consequently, the Nyquist plot will exhibit a single arc.

Case (3): σgb ~ σbulk

For case (3), in which the grain boundary conductivity and the bulk conductivity of a material with typical microstructure are almost similar to those in case (1), σbulk > σgb. Eq. (6) is reduced to Eq. (7), and Eq. (4) may be expressed as Eq. (8). The case in which two arcs are obtained in the Nyquist plot is almost the same as case (1): if (i) R1 is different from R2 by a factor of 10 to 1000 times, and (ii) w0,bulk is significantly different from w0,gb. According to Eq. (7), The Raito R2/R1 is 1/100 or smaller, for typical microstructures. The ratio is relatively small but not too small to be indistinguishable in the Nyquist plot. However, under the assumption of ɛbulk ~ ɛgb, the characteristic frequencies, w0,bulk and w0,gb, are almost identical. As a result, only single arc will be observed. In addition, if σgb is almost the same as σbulk, the σ1 obtained from the single arc will be within 2% of the σbulk. In summary, only for σbulk > σgb, two arcs can be observed.

3.3. Electrochemical Impedance Spectroscopy

The ionic conductivity in the temperature range from 600 to 250°C was obtained by impedance analysis using the brick layer model. Since the electric conductivity of a ceramic material is thermally activated, the following Arrhenius equation was used:
where Ea denotes the activation energy needed for ionic conduction, σ0 is the pre-exponential factor, and k is the Boltzmann constant. The activation energy was obtained from the Arrhenius plot (Fig. 7). As shown in Table 1, the grain boundary activation energy (1.16 eV) of the YSZ polycrystals is higher than bulk activation energy (1.06 eV). Similarly, for GDC polycrystals, the grain boundary activation energy (0.97 eV) is higher than bulk activation energy (0.68 eV). In Fig. 8, an impedance spectra was obtained at low-temperature because the grain boundary arc can be obtained at a low temperature. Two arcs of the bulk and the grain boundaries in polycrystalline YSZ were obtained (Fig. 8(a)). Since two arcs, which represented in the polycrystalline, corresponds to Case 1 (σbulk > σgb) of the brick layer model. Only one arc corresponding to the bulk was obtained in the single crystal (Fig. 8(b)). Also, for polycrystalline GDC, two arc of the bulk and the grain boundary was obtained at 260°C in the Nyquist plot (Fig. 8(c)), which corresponds to Case 1 (σbulk > σgb). The impedance spectra data for single crystal GDC were obtained from the previous study because we cannot find GDC single crystal30) As expected, only single arc is obtained the single crystal GDC because of the absence of the grain boundary. As can be seen in Fig. 9(d), (e), and (f), although ESB is polycrystalline material, grain boundary arc cannot be obtained in the Nyquist plot. ESB did not have a grain boundary blocking effect caused by the space charge layer because ESB has no aliovalent dopant which causes segregation at the grain boundaries, in contrast to acceptor doped zirconia and acceptor doped ceria (Fig. 1). We believed that CESB (Eq. (1b)) will have a grain boundary effect, because the segregation of CaBi at the grain boundary will make space charge layer similar to the case of acceptor doped zirconia and ceria.12-15) Likewise, we also believed that ZESB (Eq. (1a)) have a grain boundary effect because the segregation of CaBi at the grain boundary will cause a space charge layer. However, only single arc, not two arcs is obtained in the Nyquist plot form both CESB and ZESB. This means that the blocking effect due to the space charge does not exist in δ-Bi2O3. The resistance of the ESB at 275°C is 132.6 kΩcm, but that of CESB is lower, 75.6 kΩcm. The activation energy of CESB is 1.23 eV, which is also lower than that of ESB (1.33 eV). The resistance of ZESB at 275°C is 147 kΩcm, which is about 10% higher than that of ESB. The activation energy of ZESB is 1.31 eV, which was similar to that of ESB (1.33 eV). The lower resistance and the lower activation of CESB may be due to the increased oxygen vacancy concentration resulting from acceptor doping. The increased resistance in ZESB probably is due to the decreased oxygen vacancy concentration resulting from donor doping. This result is consistent with a previous study conducted with Y-stabilized δ-Bi2O3 doped with Zr or Ca.31) The absence of the space charge effect in the cubic bismuth oxides, regardless of the acceptor or donor doping, may have been because of the high oxygen vacancy concentration of δ-Bi2O3 itself (25%).8) The oxygen vacancy depletion in the space charge layer was proposed as the cause of the grain boundary blocking effect.2) In δ-Bi2O3, the oxygen vacancy depletion in the space charge layer may be negligible, because the oxygen vacancy concentration of δ-Bi2O3 was much higher (25%) than that of 8YSZ (oxygen vacancy concentration: 8%) and GDC (oxygen vacancy concentration: 10%). In addition, according to the brick layer model, the cases in which a single impedance arc is obtained are Case 2 (σbulk ~ σgb) and Case 3 (σbulk < σgb). Therefore, the grain boundary ionic conductivity of δ-Bi2O3 should be similar to or higher than the bulk ionic conductivity. because of the high oxygen vacancy concentration and the high ionic conductivity at the grain boundary, δ-Bi2O3 is almost free from the space charge effect, unlike other fluorite-type structure materials, thus it does not show the grain boundary blocking effect. An oxygen diffusion study of Bi2O3 conducted by oxygen tracer diffusion measurements demonstrated that Grain boundary ion diffusion in α-Bi2O3 is three to four magntude higher than bulk at 600°C, which is similar to the oxygen ion diffusion rate in bulk Ce0.7Gd0.3O1.85.32) In short, the main mechanism of the ionic conduction in δ-Bi2O3 may be through the grain boundaries. To prove this theory more directly, further studies need to be conducted to observe the dopant segregation at the grain boundaries of ZESB and CESB through TEM and EELS and the space charge potential through KFM, which will demonstrate more direct experimental evidences that Space charge effect is negligible in cubic bismuth oxide.

4. Conclusions

In this work, an electrochemical impedance analysis was performed to investigate the grain boundary blocking effect due to the space charge in fluorite-type structured YSZ, GDC, ESB, ZESB, and CESB. The results showed that two distinguishable arcs were obtained in the Nyquist plot of polycrystalline YSZ and GDC, which confirmed the presence of the grain boundary blocking effect. The single-crystal materials with no grain boundary have only one arc, as expected. However, polycrystalline ESB and ZESB, and CESB have only one arc, indicating the absence of the grain boundary blocking effect caused by the space charge. The absence of the blocking effect in δ-Bi2O3 may be because the intrinsic oxygen vacancy concentration in δ-Bi2O3 is as high as 25% due to crystal structure. In addition, by applying the brick layer model for the impedance analysis, we denmonstrate that grain boundary ionic conductivity of δ-Bi2O3 is or even higher than bulk ionic conductivity (σbulkσbg ). Therefore, in this study we indirectly demonstrated that for δ-Bi2O3, grain boundary may be a main ionic conductivity path unlike other fluorite-type materials and grain boudnary blocking effect is absence using impedance analysis.


This work was supported by the National Research Foundation of Korea (Grant NO. 2014R1A4A1003712 (Basic Research Laboratory Project)) and the Ministry of Trade, Industry and Energy (Grant NO. 10065691). The authors acknowledge Hye-Sung Kim and Hyewon Ryoo for their fruitful comments.

Fig. 1
Crystal structure of (a) δ-Bi2O3, (b) Gd doped ceria. Yttria stabilized zirconia (YSZ) has the same structure as (b).
Fig. 2
Powder X-ray diffraction patterns of ESB, ZESB and CESB after 800°C calcination with index from ICDD card 00-034-0377, 03-065-3319.
Fig. 3
SEM image showing the cross section microstructures: (a) GDC with average grain size of 1.65 μm (b) polycrystalline YSZ with average grain size of 2.85 μm (c) single crystal YSZ, (d) ESB with average grain size of 6.51 μm (e) ZESB with average grain size of 4.1 μm (f) CESB with average grain size of 2.3 μm.
Fig. 4
A typical Nyquist plot and equivalent circuit of a polycrystalline material with brick layer model. Q is the constant phase element and R is the resistance.
Fig. 5
“Brick layer” model of a polycrystalline material. Grains are assumed to be cube-shaped, and grain boundaries exist as flat layers between grains.29)
Fig. 6
Equivalent circuit models of a polycrystalline material with brick layer model. (a) Each component explicitly included in the circuit; (b) simplified equivalent circuit.
Fig. 7
Bulk ionic conductivity of all samples. Data are plotted in Arrhenius form.
Fig. 8
(a-d) Nyquist impedance plots obtained from polycrystalline YSZ, single crystal YSZ, polycrystalline GDC, and single crystalline Ce0.69Gd0.31O2−δ (GDC) impedance spectra data; (d) is from ref. 30.
Fig. 9
(a-c) Impedance spectra from polycrystalline ESB, ZESB and CESB.
Table 1
Activation Energy of Each Sample
polycrystalline YSZ single crystal YSZ polycrystalline GDC polycrystalline ESB polycrystalline ZESB polycrystalline CESB
Bulk Ea (eV) 1.06 1.16 0.68 1.33 1.31 1.24
G.b Ea (eV) 1.16 - 0.97 - - -


1. ED. Wachsman, and KT. Lee, “Lowering the Temperature of Solid Oxide Fuel Cells,” Science, 334 [6058] 935-39 (2011).
2. AM. Azad, S. Larose, and SA. Akbar, “Bismuth Oxide-based Solid Electrolytes for Fuel Cells,” J Mater Sci, 29 [16] 4135-51 (1994).
3. VV. Kharton, FMB. Marques, and A. Atkinson, “Transport Properties of Solid Oxide Electrolyte Ceramics: A Brief Review,” Solid State Ionics, 174 [1] 135-49 (2004).
4. P. Shuk, HD. Wiemhöfer, U. Guth, W. Göpel, and M. Greenblatt, “Oxide Ion Conducting Solid Electrolytes based on Bi2O3 ,” Solid State Ionics, 89 [3-4] 179-96 (1996).
5. NM. Sammes, GA. Tompsett, H. Nafe, and F. Aldinger, “Bismuth based Oxide Electrolytes-Structure and Ionic Conductivity,” J Eur Ceram Soc, 19 [10] 1801-26 (1999).
6. M. Mogensen, NM. Sammers, and GA. Tompsett, “Physical, Chemical, and Electrochemical Properties of Pure and Doped Ceria,” Solid State Ionics, 129 [1] 63-94 (2000).
7. BCH. Steele, “Material Science and Engineering: The Enabling Technology for the Commercialisation of Fuel Cell Systems,” J Mater Sci, 36 [5] 1053-68 (2001).
8. PD. Battle, CRA. Catlow, JW. Heap, and LM. Moroney, “Structural and Dynamical Studies of δ-Bi2O3 Oxide-Ion Conductors II. A Structural Comparison of (Bi2O3)1−x(M2O3)x for M = Y, Er and Yb,” J Solid State Chem, 67 [1] 42-50 (1987).
9. X. Guo, W. Sigle, and J. Maier, “Blocking Grain Boundaries in Yttria-Doped and Undoped Ceria Ceramics of High Purity,” J Am Ceram Soc, 86 [1] 77-87 (2003).
10. HJ. Avila-Paredes, K. Choi, CT. Chen, and S. Kim, “Dopant-Concentration Dependence of Grain-Boundary Conductivity in Ceria: A Space-Charge Analysis,” J Mater Chem, 19 [27] 4837-42 (2009).
11. X. Guo, and J. Maier, “Grain Boundary Blocking Effect in Zirconia: A Schottky Barrier Analysis,” J Electrochem Soc, 148 [3] E121-26 (2001).
12. X. Guo, W. Sigle, J. Fleig, and J. Maier, “Role of Space Charge in the Grain Boundary Blocking Effect in Doped Zirconia,” Solid State Ionics, 154 555-61 (2002).
13. NM. Beekmans, and L. Heyne, “Correlation between Impedance, Microstructure and Composition of Calcia-Stabilized Zirconia,” Electrochim Acta, 21 [4] 303-10 (1976).
14. SPS. Badwal, “Grain Boundary Resistivity in Zirconia-based Materials: Effect of Sintering Temperatures and Impurities,” Solid State Ionics, 76 [1-2] 67-80 (1995).
15. M. Aoki, YM. Chiang, I. Kosacki, L. Lee, H. Tuller, and Y. Liu, “Solute Segregation and Grain-Boundary Impedance in High-Purity Stabilized Zirconia,” J Am Ceram Soc, 79 [5] 1169-80 (1996).
16. X. Guo, and R. Waser, “Electrical Properties of the Grain Boundaries of Oxygen Ion Conductors: Acceptor-doped Zirconia and Ceria,” Prog Mater Sci, 51 [2] 151-210 (2006).
17. S. Kim, J. Fleig, and J. Maier, “Space Charge Conduction: Simple Analytical Solutions for Ionic and Mixed Conductors and Application to Nanocrystalline Ceria,” Phys Chem Chem Phys, 5 [11] 2268-73 (2003).
18. Y. Lei, Y. Ito, ND. Browning, and TJ. Mazanec, “Segregation Effects at Grain Boundaries in Fluorite-Structured Ceramics,” J Am Ceram Soc, 85 [9] 2359-63 (2002).
19. W. Lee, HJ. Jung, MH. Lee, YB. Kim, JS. Park, R. Sinclair, and FB. Prinz, “Oxygen Surface Exchange at Grain Boundaries of Oxide Ion Conductors,” Adv Funct Mater, 22 [5] 965-71 (2012).
20. P. Duran, JR. Jurado, C. Moure, N. Valverde, and BCH. Steele, “High Oxygen Ion Conduction in Some Bi2O3-Y2O3(Er2O3) Solid Solutions,” Mater Chem Phys, 18 [3] 287-94 (1987).
21. MF. Yan, RM. Cannon, and HK. Bowen, “Space Charge, Elastic Field, and Dipole Contributions to Equilibrium Solute Segregation at Interfaces,” J Appl Phys, 54 [2] 764-78 (1983).
22. RD. Shannon, “Revised Effective Ionic Radii and Systematic Studies of Interatomic Distances in Halides and Chalcogenides,” Acta Cryst A, 32 751-67 (1976).
crossref pdf
23. FA. Kröger, and HJ. Vink, “Relations betwwen the Concentration of Imperfections in Crystalline Solids,”; pp. 307-435 in Solid State Physics, 3 In : Seitz F, Turnbull D, editors, Academic press, New York, 1956.
24. HA. Harwig, and AG. Gerards, “The Polymorphism of Bismuth Sesquioxide,” Thermochim Acta, 28 [1] 121-31 (1979).
25. MJ. Verkerk, K. Keizer, and AJ. Burggraaf, “High Oxygen Ion Conduction in Sintered Oxides of the Bi2O3-Er2O3 System,” J Appl Electrochem, 10 [1] 81-90 (1980).
26. N. Bonanos, BCH. Steele, and EP. Butler, Impedance Spectroscopy; 1st ed. pp. 191-238 In : MacDonald JR, editor, Wiley and Sons, New York, 1988.

27. H. Näfe, “Ionic Conductivity of ThO2-and ZrO2-based Electrolytes between 300 and 2000 K,” Solid State Ionics, 13 [3] 255-63 (1984).
28. GM. Christie, and FPF. Van Berkel, “Microstructure-Ionic Conductivity Relationships in Ceria-Gadolinia Electrolytes,” Solid State Ionics, 83 [1-2] 17-27 (1996).
29. SM. Haile, LW. David, and J. Campbell, “The Role of Microstructure and Processing on the Proton Conducting Properties of Gadolinium-doped Barium Cerate,” J Mater Res, 13 [6] 1576-95 (1998).
30. E. Ruiz-Trejo, JD. Sirman, YM. Baikov, and JA. Kilner, “Oxygen Ion Diffusivity, Surface Exchange and Ionic Conductivity in Single Crystal Gadolinia Doped Ceria,” Solid State Ionics, 113 565-69 (1998).
31. KZ. Fung, and AV. Virkar, “Phase Stability, Phase Transformation Kinetics, and Conductivity of Y2O3-Bi2O3 Solid Electrolytes Containing Aliovalent Dopants,” J Am Ceram Soc, 74 [8] 1970-80 (1991).
32. RD. Bayliss, SN. Cook, S. Kotsantonis, RJ. Chater, and JA. Kilner, “Oxygen Ion Diffusion and Surface Exchange Properties of the α-and δ-phases of Bi2O3 ,” Adv Energy Mater, 4 [10] 1301575(2014).
PDF Links  PDF Links
PubReader  PubReader
ePub Link  ePub Link
Full text via DOI  Full text via DOI
Download Citation  Download Citation
CrossRef TDM  CrossRef TDM
Related article
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI