Journal of the Korean Ceramic Society 2004;41(1): 51.
doi: https://doi.org/10.4191/kcers.2004.41.1.051
뮬라이트 휘스커의 제조와 특성
이홍림, 심일용, 강종봉
경남대학교 신소재공학부
Preparation and Characterization of Mullite Whiskers
Hong-Lim Lee, Il-Yong Shim, Jong-Bong Kang
Division of Advanced Materials Engineering, Kyungnam University
Mullite whiskers were synthesized using $Al(OH)_3$, amorphous $SiO_2$ and $AIF_3$ as starting materials by a vapor-solid reaction at relatively low temperature of $1100^{circ}C$. Leaflet Fluorotopaz was observed for the specimen heat-treated at $800^{circ}C$. Fluorotopaz was decomposed at $1000^{circ}C$ and only mullite phase was observed for the specimen sintered at $1100^{circ}C$ and above. It was found that the synthesized mullite at $1200^{circ}C$ had grown to [001] direction and side planes were the {110}. The distance of (110} plane was $5.34^{AA}C$. The amounts of $Al_2O_3$ in mullite was 73.56(1.39)wt%.
Key words: Mullite whiskers, Fluorotopaz, Vapor-solid reaction
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI