Journal of the Korean Ceramic Society 2002;39(5): 511.
doi: https://doi.org/10.4191/kcers.2002.39.5.511
졸-겔 공정에 의한 YMnO3 박막의 전기적 특성
김응수, 김병규, 김유택
경기대학교 재료공학과
Electrical Properties of YMnO3 Thin Film by Sol-gel Process
Eung Soo Kim, Beng-Gu Kim, Yoo-Taek Kim
Department of Materials Engineering, Kyonggi University
Hexagonal $YMnO_3$ thin films were prepared from $Y(NO_3)_3{cdot}5H_2O$ and $Mn(CH_3CO_2)_2{cdot}4H_2O$ as starting materials on the Si(100) substrates by the sol-gel method. The crystal structure and the electrical properties of the $YMnO_3$ thin films were investigated as a function of heat treatment temperature, the amount of water(Rw) of hydrolysis and the addition of catalysis. The crystallization of the $YMnO_3$ thin film began at 700${circ}C$ and completed at 800${circ}C$ for 1 h. The c-axis (0001) preferred orientation of hexagonal $YMnO_3$ was detected for the $YMnO_3$ thin films with Rw=6 and that was decreased for the $YMnO_3$ thin films with Rw=1 and Rw=12. The crystallinity and preferred orientation of the $YMnO_3$ thin films were depended on the addition of acid and/or alkali catalysis, which, in turn, the preferred orientation of c-axis was decreased and the orthorhombic phase of $YMnO_3$ was detected to the specimens with the addition of catalysis. The $YMnO_3$ thin film with Rw=6 showed good leakage current density of $1.2{times}10-8 A/cm^2$ at the applied voltage of 0.2V and the leakage current density was not changed drastically with applied voltage.
Key words: Sol-gel method, Hexagonal $YMnO_3$, Orthorhombic $YMnO_3$ Preferred orientation, Rw ratio
Editorial Office
Meorijae Bldg., Suite # 403, 76, Bangbae-ro, Seocho-gu, Seoul 06704, Korea
TEL: +82-2-584-0185   FAX: +82-2-586-4582   E-mail: ceramic@kcers.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Ceramic Society.                      Developed in M2PI